Total oxidation of propene at low temperature over Co3O4–CeO2 mixed oxides: Role of surface oxygen vacancies and bulk oxygen mobility in the catalyti…
2008
Liotta, L. F. Ousmane, M. Di Carlo, G. Pantaleo, G. Deganello, G. Marci, G. Retailleau, L. Giroir-Fendler, A.; Co3O4, CeO2 and Co3O4-CeO2 mixed oxides with Co/Ce nominal atomic ratio 0.1:5, prepared by co-precipitation method with sodium carbonate, were tested in the oxidation of propene under lean condition and the catalyst stability was checked by performing three consecutive heating-cooling cycles. Characterization of the textural properties were performed by surface area measurement BET, X-ray diffraction (XRD) and scanning electron microscopy (SEM) measurements. Among the Co3O4-CeO2 mixed oxides, Co3O4 (30 Wt%)-CeO2 (70 wt%) gives the best activity attaining full propene conversion at …
Honeycomb supported Co3O4/CeO2 catalysts for CO/CH4 emissions abatement: effect of low Pd-Pt content on the catalytic activity
2007
Abstract A structured Co3O4–CeO2 composite oxide, containing 30% by weight of Co3O4, has been prepared over a cordieritic honeycomb support. The bimetallic, Pd–Pt catalyst has been obtained by impregnation of the supported Co3O4–CeO2 with Pd and Pt precursors in order to obtain a total metal loading of 50 g/ft3. CO, CH4 combined oxidation tests were performed over the catalyzed monoliths in realistic conditions, namely GHSV = 100,000 h−1 and reaction feed close to emission from bi-fuel vehicles. The Pd–Pt un-promoted Co3O4–CeO2 is promising for cold-start application, showing massive CO conversion below 100 °C, in lean condition. A strong enhancement of the CH4 oxidation activity, between 4…